DIN 115CrV3 Silver Steel

DIN 115CrV3 (SILVER STEEL WITH VANADIUM) IS A  HIGH QUALITY ALLOY STEEL FOR COLD WORKING.

CHEMICAL COMPOSITION:

C : 1,10 - 1,25; Mn 0,20 -0,40 ; Si 0,15 – 0,30 ; P MAX. 0,030 ; S MAX. 0,030 ; Cr 0,50– 0,80 ; V 0,07 – 0,12 ;

DELIVERY : HEAT TREATMENT ANNEALED 219 / 250HB

SURFACE FINISHING : CENTERLESS GROUND Ra 0.8um

DIAMETERS : FROM 1mm TO 40mm

DIAMETER TOLERANCE : AS PER DIN 175 OR EQUIVALENT ISO h9 .

AS PER REQUIREMENT WITH TOLERANCES h 8 OR h 7

DELIVERY LENGTHS: FROM 1METER TO 3 METERS

QUALITY : HIGH PRECISION EN SIZES ; OPTIMAL MACHINABILITY ON ANNEALEAD STATUS; DEFECTS AND DECABURISATION FREE ; EXCELENT FINISHING AND STRAIGHTNESS.

Properties :

DIN 115CrV3 Chromium - vanadium alloyed cold work tool steel with high wear resistance,high edge holding properties,simple heat treatment, good machinability and toughness properties, bright ground and polished.

Applications :

DIN 115CrV3 Silver steel for guiding pins, small tools and structural parts in precision mechanics, button type drills and jagged bits,screw taps, milling cutters, broaching tools, piercing punches, ejector pins, twist drills, punches and taps, surgical inst-ruments, reamers, countersinks, dowels, engraving tools, metal cutting saws, axles and shafts, toothed drills, scraping tools, gear cutters, mortice, wood chisels, guide rods.

Heat Treatment :

Annealing:710 - 750 °C

Hardness after annealing:Max. 220 HB

Stress relieving:Approx. 650 °C

Hot forming:1050 - 850 °C

Hardening:780 - 810 °C or 810 - 840 °C

Quenching media:780 - 810 °C, Water

810 - 840 °C, Oil ( up to 15 mm diameter )

Hardness after quenching:64 - 66HRC

Hardness after tempering: