Products

Produce Process: Hot Rolled /Forged
Type:Plate/Round Bar/Flat Bar

Produce Process: Hot Rolled/Forged
Diameter: 60 - 500mm
Surface Treatment: Peeled/Rough Turned/Polished
Delivery Condition: Annealed / Q+T

Tensile Strength(MPA): 1860
Reduction in Area (ψ/%)： 25
Impact (J)： 23
Hardness (Anealed Condition)： ≤241HB

Tensile Strength(MPA): 1860
Reduction in Area (ψ/%): 25
Impact (J): 23
Hardness (Anealed Condition): ≤241HB

Size: Round
Dia: 6-1200mm
Process: EAF+LF+VD+Forged+Heat treatment(optional)
Heat Treatment: Normalized;Annealed;Quenched;Tempered

Size: Round
Dia: 30-1200mm
Heat Treatment: Normalized;Annealed;Quenched;Tempered
Surface Condition: Black;Peeled;Polished;Machined;Grinded;Turned;Milled

Size: 8mm-3000mm
Standard: ASTM/DIN&BS EN/JIS
Certification: ISO9001, BV,SGS, CTI, ROHS

Process: Forged from vacuum degassed ingots
Diameter: 130mm-1000mm (optional)
Length: 1000mm-12000mm Straightness: 3mm/M max(optional)
Process: EAF + LF + VD + Forged + Heat...

Size: Round
Dia: 10-500mm
Heat Treatment: As rolled, Normalized.Annealed, Q+T
Surface Condition: Black;Machined

Density g/cm3: 7.85
Specific Heat Capacity J/(kg.K): 460
Electric Resistivity Ohm.mm2 /m: 0.18
Electric Conductivity Siemens.m/mm2: 5.55

Tensile Strength σ b (MPa): ≥1180
yield Strength σ s (MPa): ≥835
Elongation δ 5 (%): ≥10
Reduction of Area ψ (%): ≥45

Tensile Strength σb (MPa): ≥1175
Yield Strength σs (MPa): ≥1080
Elongation δ5 (%): ≥10
Section Shrinkage Z%: ≥45