Products

Temperature ℃: 20
Density g/cm3: 8.16
Modulus of Elasticity KN/mm2: 225
Heat Transfer Coefficient W/m℃: 24

Material: W6Mo5Cr4V2/M2/1.3343
Size: Dia3.0-200mm
Length: 3000-5000mm
Surface: Bright or black

Round Bar Size: Dia3.0-200mm
Length: 3-5m
Surface: Black or bright
Condition of Delivery: Anealling/heat treatment

The Heat Preservation Time/min: 5 ~ 15
Quenching Medium: Oil cooling
Hardness: 64 HRC Min

Grade: M42
C: 1.05-1.15
Si: 0.15-0.65
Mn: 0.15-0.40

Metric
Hardness,Rockwell C (tempered at 1150°F,quenched at 2200°F): 62
Hardness,Rockwell C (as hardened,quenched at 2200°F): 65
Compressive Yield Strength (when tempered at...

C: 0.80-0.90
Si: 0.15-0.45
Mn: 0.15-0.40
Cr: 3.80-4.40

JIS: SUM24L
C: 0.15max
Si: 0.15-0.35
Mn: 0.85-1.15

Tensile Strength σb (MPa): ≥42
Reduction of Area ψ (%): ≥34
Elongation δ5 (%): ≥22
Hardness HB: ≤160

Grade: 1.0718
C: 0.14
Si: 0.05
Mn: 0.90-1.30

Round Bars: 5mm-130mm
Suqare Bar: 6*6mm-100*100mm
Flat Bars: 3mm*20mm-50mm*100mm
Hex Bars: 6mm-100mm