Din 1.2888 Mold Steel

Dear valued merchant,

 

We are excited to introduce our exclusive product, the Din 1.2888 Mold Steel Equivalent. This premium-grade mold steel is specifically designed to meet the highest standards of the industry, providing unparalleled durability, strength, and resistance to wear and tear.

 

As a leading manufacturer based in China, our primary focus is to deliver top-quality products that cater to the needs of our clients across the globe. Our team of qualified engineers and technicians have worked tirelessly to develop a superior-grade mold steel that can stand the test of time and withstand the harsh conditions that are often encountered in the manufacturing industry.

 

At its core, the Din 1.2888 Mold Steel Equivalent is infused with high levels of alloy and carbon, allowing it to deliver exceptional performance in the most demanding environments. Its unique composition allows it to retain its properties even when subjected to extreme temperatures, ensuring that it remains stable and reliable throughout its lifetime.

 

Some of the key features of this product include:

 

1. High Yield Strength: With a yield strength of up to 1200Mpa, the Din 1.2888 Mold Steel Equivalent is one of the toughest and most durable materials that you can find in the market today. Its high strength-to-weight ratio makes it ideal for use in a wide range of applications, including tooling, die casting, and molding.

 

2. Superior Wear Resistance: Our mold steel boasts an exceptional level of wear resistance, thanks to its high carbon content. This makes it an ideal choice for use in industries where abrasive materials are frequently used, such as in the production of automotive parts, dies, and molds.

 

3. Excellent Machinability: Apart from its durability and wear resistance, the Din 1.2888 Mold Steel Equivalent is also incredibly easy to machine, providing exceptional finishing and excellent surface quality. This makes it a popular choice among craftsmen and machinists who demand precision and accuracy.

 

4. Corrosion Resistance: Our mold steel is designed to withstand harsh environmental conditions, making it an ideal choice for use in marine or industrial applications where corrosion is a potential issue. Its unique composition provides it with superior resistance against oxidation, pitting, and crevice corrosion.

 

In conclusion, the Din 1.2888 Mold Steel Equivalent is one of the most reliable and versatile materials in the industry. Its unique composition makes it a popular choice among manufacturers who demand a high level of performance, durability, and reliability. We are confident that our product will exceed your expectations and provide you with the level of quality and value that you deserve.

 

Thank you for considering our product, and we look forward to serving you.

 

Best regards,

 

[Your Company]

 

 

 

Why choose us?

• We have a track record of providing quality Die Steel Bar products and services to businesses around the world.
• Our company has first-class scientific and technological talents, equipped with domestic advanced product quality testing equipment.
• Our factory is equipped with state-of-the-art machinery to produce Die Steel Bar products that meet the highest standards of quality.
• In order to meet the market development needs, we will constantly adjust the product structure and update the production process, and we will provide all convenience and preferences then.
• We understand the importance of quality control and follow strict procedures to ensure the quality of our Die Steel Bar products.
• We are committed to promoting the development of the world's Din 1.2888 Mold Steel Equivalent industry and building an internationally influential technology Din 1.2888 Mold Steel Equivalent brand.
• At our factory, we use advanced production techniques to produce Die Steel Bar products that are of the highest quality.
• Over the years, we have worked hard to promote the transformation of enterprises from small to large, from single structure to diversified operation, and from rapid development to strong enterprise.
• As a customer-focused company, we are committed to delivering the best possible Die Steel Bar products and services.
• Being a young growing company, we might not the best, but we are trying our best to be your good partner.

 

Relevant Steel Specifications of AISI T4 High Speed Tool Steels

Country	USA	German	Japan
Standard	ASTM A600	DIN EN ISO 4957	JIS G4403
Grades	T4/T12004	S 18-1-2-5/1.3255	SKH3

 

AISI T4 Tool Steel and Equivalents' Chemical Composition

ASTM A600	C		Mn		P	S	Si		Cr		V		W		Mo		Co
T4	0.70	0.80	0.10	0.40	0.03	0.03	0.20	0.40	3.75	4.50	0.80	1.20	17.50	19.00	0.40	1.00	4.25	5.75
DIN ISO 4957	C		Mn		P	S	Si		Cr		V		W		Mo		Co
S 18-1-2-5/1.3255	0.75	0.83	…	0.40	0.03	0.03	…	0.45	3.80	4.50	0.80	1.20	17.50	18.50	0.50	0.80	4.50	5.50
JIS G4403	C		Mn		P	S	Si		Cr		V		W		Mo		Co
SKH3	0.73	0.83	…	0.40	0.03	0.03	…	0.45	3.80	4.50	0.80	1.20	17.00	19.00	…	…	4.50	5.50

 

Mechanical Properties of T-4 Steel

Properties	Metric	Imperial
Modulus of elasticity	190-210 GPa	27557-30458 ksi
Poisson's ratio	0.27-0.30	0.27-0.30

 

Thermal Properties of T4 Tool Steels

Properties	Metric	Imperial
Thermal expansion co-efficient	11.9 µm/m°C	6.6 µin/in°F

 

Forging of ASTM T4 Tool Steel Materials

Forging of T4 steel can be carried out from 850 to 1120°C (1775 to 2100°F).

Preheat T4 steel material uniformly and slowly to 860-880°C.

Increase the forging temperature up to 1050-1120°C.

T4 hss tool steel should be cooled very slowly after forging.

 

AISI/ASTM T4 Tool Steel Heat Treatment and Properties

Hardening:

Harden T4 high speed tool steel from a temperature of 1260-1290oC followed by oil, air quenching or warm bath at 550oC. Hardness after quenching is 63-66 HRC.

Annealing:

T4 steel should be annealed after hot working. Increase the temperature of T4 high speed steel to 860°C(Max220°C per hour). Hold at the temperature and then cool slowly with the furnace. The annealed hardness achieved should be below HB255.

Tempering:

Tempering temperature: 2x 560-580oC. Hardness after tempering is 64-65 HRC.